There is no temper in the steel yet, The speed of the cutter should never heat steel to the point of temper you would be throwing sparks at that point, plus my cuttes wont cut hardend steel I have not heat treated it yet. The final sharpen will be with a stone once it has been heat treated, I expect it to have a hardness similar to a file but not as brittle.